The influence of high additions of manganes up to 11% Mn for grain refining of α+β brasses

Thumbnail
Oglądaj/Otwórz
Autor:
Malczewski, Piotr
Kurtyka, Paweł
Dutkiewicz, Jan
Wydawca:
Institute of Technology, Pedagogical University, Cracow, cop. 2006
Źródło: Problems of modern techniques in aspect of engineering and education / [ed. board Paweł Kurtyka et al.]. - Cracow, 2006. - S. [273]-277.
Język: en
Słowa kluczowe:
α+β brasses
superplastic deformation
strain rate sensitivity
Data: 2006
Metadata
Pokaż pełny rekord
Streszczenie
The brasses containing 6 and 11 wt. % of Mn were quenched from the β phase range and cold rolled. Then, samples were annealed at the temperature range 450-600°C leading to the α+β structure and the grain size 3,5 μm. Tensile tests of alloys containing 6-11% Mn showed good superplastic properties at temperature 500°C where the value of strain rate sensitivity coefficient m attained values of 0.65 for the alloy containing 6% Mn and 0.64 for the alloy containing 11% Mn.
URI
http://hdl.handle.net/11716/1422